Dispersoid particles precipitated during the solutionizing course of Al-12wt%Si-4wt%Cu-1.2wt%Mn alloy and their influence on high temperature strength

Yiyun Hu   Pavel Petrov   Uday S. Dixit   Yunyi Tang   Guangjin Li   Hengcheng Liao   Xiaojing Suo  
Abstract

Microstructure evolution during the solutionizing course of Al-12wt%Si-4wt%Cu-1.2wt%Mn alloy was characterized by XRD and TEM-SAD (selected area diffraction), and the contribution of dispersoid Mn-rich precipitates to high temperature strength is discussed qualitatively. Fine and dispersoid Al20Cu2Mn3 (orthorhombic structure, a=2.34nm, b=1.32nm, c=0.75nm) and Al15Mn3Si2 (body center cubic structure, a=2.259nm) particles are found to precipitate during the solutionizing course. Both the solutionizing temperature and time have an important influence on the precipitation behavior of these particles. The number density of the precipitates first increased and then decreased with the solutionizing temperature. It decreased monotonically with the solutionizing time. The variation trend of the size of precipitates with temperature and time was opposite to that of the number density. The precipitation of these dispersoid Al20Cu2Mn3 and Al15Mn3Si2 particles has a considerable influence on the high temperature strength.

Original Text (This is the original text for your reference.)

Dispersoid particles precipitated during the solutionizing course of Al-12wt%Si-4wt%Cu-1.2wt%Mn alloy and their influence on high temperature strength

Microstructure evolution during the solutionizing course of Al-12wt%Si-4wt%Cu-1.2wt%Mn alloy was characterized by XRD and TEM-SAD (selected area diffraction), and the contribution of dispersoid Mn-rich precipitates to high temperature strength is discussed qualitatively. Fine and dispersoid Al20Cu2Mn3 (orthorhombic structure, a=2.34nm, b=1.32nm, c=0.75nm) and Al15Mn3Si2 (body center cubic structure, a=2.259nm) particles are found to precipitate during the solutionizing course. Both the solutionizing temperature and time have an important influence on the precipitation behavior of these particles. The number density of the precipitates first increased and then decreased with the solutionizing temperature. It decreased monotonically with the solutionizing time. The variation trend of the size of precipitates with temperature and time was opposite to that of the number density. The precipitation of these dispersoid Al20Cu2Mn3 and Al15Mn3Si2 particles has a considerable influence on the high temperature strength.

+More

Cite this article
APA

APA

MLA

Chicago

Yiyun Hu, Pavel Petrov, Uday S. Dixit, Yunyi Tang, Guangjin Li,Hengcheng Liao, Xiaojing Suo,.Dispersoid particles precipitated during the solutionizing course of Al-12wt%Si-4wt%Cu-1.2wt%Mn alloy and their influence on high temperature strength. 699 (0),.

Disclaimer: The translated content is provided by third-party translation service providers, and IKCEST shall not assume any responsibility for the accuracy and legality of the content.
Translate engine
Article's language
English
中文
Pусск
Français
Español
العربية
Português
Kikongo
Dutch
kiswahili
هَوُسَ
IsiZulu
Action
Recommended articles

Report

Select your report category*



Reason*



By pressing send, your feedback will be used to improve IKCEST. Your privacy will be protected.

Submit
Cancel