In this study, the effect of different shielding gas and laser scanning velocity on the resulting retained austenite (RA) content and tribomechanical properties of AISI 8620 steel were investigated. RA generation was comparatively lower at higher scanning velocity and with argon as the shielding gas due to lower beam interaction time and inert environment. Varied heat input and differing reaction volume resulted in different hardness levels on these samples. Air shielded samples showed slightly higher friction coefficient than the other samples due to higher surface roughness and shearing of oxide layers. The nitrogen shielded samples exhibited the best wear resistance among all samples, which was attributed to nitride formation on surface and to high hardness resulting from the laser treatment.

+More

tribomechanical properties hardness friction coefficient wear resistance reaction ra generation laser scanning velocity retained austenite ra content shielding gas nitride formation 8620 surface roughness oxide beam interaction

Sougata Roy, Jingnan Zhao, Sriram Sundararajan, Pranav Shrotriya,.Effect of laser treatment parameters on surface modification and tribological behavior of AISI 8620 steel. 112 (0),.

Sougata Roy, et al."Effect of laser treatment parameters on surface modification and tribological behavior of AISI 8620 steel" 112

Sougata Roy, Jingnan Zhao, Sriram Sundararajan, Pranav Shrotriya,"Effect of laser treatment parameters on surface modification and tribological behavior of AISI 8620 steel"